The Effect of Laser Combined With Pulp-capping Agents on Direct Pulp Capping

Exposed area was sealed with a self-hardening calcium hydroxide paste then final restoration was completed using a resin-modified glass ionomer and a nanohybrid composite resin

After the exposed area was irradiated with Er,Cr:YSGG laser at an energy level of 0,5 W, a repetition rate of 20 Hz, 140 µs pulse duration with 0% water and 45% air for 10 s, it was sealed with a self-hardening calcium hydroxide paste.Then final restoration was completed using a resin-modified glass ionomer and a nanohybrid composite resin

TheraCal LC was applied directly to the exposed pulp with a needle tip syringe in incremental layers that was not to exceed 1 mm in depth. Then final restoration was completed using a resin-modified glass ionomer and a nanohybrid composite resin

After the exposed area was irradiated with Er,Cr:YSGG laser at an energy level of 0,5 W, a repetition rate of 20 Hz, 140 µs pulse duration with 0% water and 45% air for 10 s, TheraCal LC was used to seal the treated area. Then final restoration was completed using a resin-modified glass ionomer and a nanohybrid composite resin